Learn more about the integral components of our ceramic heating element.
Technology / Material properties
Our 100% ceramic heating elements made from silicon nitride and aluminum nitride have a number of advantages in comparison to metallic heating elements. Owing to the low thermal capacity of the material due to its low-density, ceramic material has a low heat capacity and therefore is well suited to handle temperatures up to 1 000 °C with very little energy consumption.
This extraordinary technology, which implements ceramic material able to conduct electricity uniformly sintered with an insulated ceramic housing, is able to deliver high performance consistently. Highly resistant to wear and oxidation, these ceramics guarantee outstanding durability and long life as well.
|max. temperature (Tmax)||°C||1 000||1 000|
|thermal conductivity (λ)||W/mK||40||140|
|temperature shock resistance (ΔT)||K||500||400|
|emissivity (1100 °C) (ε)||-||0.96||0.90|
|Young's modulus (E)||GPa||320||310|
|bending strength (δBB)||MPa||400||200|
|compressive strength (δD)||MPa||2 000||1 200|
|coefficient of thermal expansion (α)||10-6 K-1||3||5|
|specific heat (cp)||J/kgK||750||740|
|porosity (100 - % t.D.)||%||0||0|
|critical stress intensity factor (KIc)||MPa m½||6||3.3|
|Weibull – modulus (m)||-||7.9||6|
The thermal shock resistance depends on the geometric shape of the heater.
|in still air||W/cm2||15|
|in moving air (40 m/s)||W/cm2||25|
|resistivity||Ω cm||5 · 10-3 - 5 · 10-1||5 · 10-3 – 2 · 10-1|
|isolation resistivity||Ω mm (20 °C)||1013||1013|
Fully ceramic heating elements are long-wave infrared heaters with a maximum emission of 5 to 10 µm and a radiation coefficient of ε > 0.9.
The high compressive strength of 2 000 MPa and the high Young's modulus of 300 GPa of the Silicon nitride ceramic material are maintained at temperatures up to 1 000 °C. There is hardly any self-deformation.